Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 7
Page 207
... Boiler feed water , Boiler condensates , Vapour ( kg / cm2 ) ( b ) pH ( ) C1 ( ppm ) Relating to the Stress Corrosion Cracking of Heat Exchangers Used 207 H. Okada Corrosion Reviews.
... Boiler feed water , Boiler condensates , Vapour ( kg / cm2 ) ( b ) pH ( ) C1 ( ppm ) Relating to the Stress Corrosion Cracking of Heat Exchangers Used 207 H. Okada Corrosion Reviews.
Page 217
... boiler feed water ( BFW ) . The tube materials in Figures 3 to 5 relate to both Types 304 and 316 stainless steels . In the diagrams , the numbers ( 1 ) , ( 2 ) and ( 3 ) indicate the degrees of accuracy associated with calculating tube ...
... boiler feed water ( BFW ) . The tube materials in Figures 3 to 5 relate to both Types 304 and 316 stainless steels . In the diagrams , the numbers ( 1 ) , ( 2 ) and ( 3 ) indicate the degrees of accuracy associated with calculating tube ...
Page 190
... Boiler Recovery Boiler System Recovery Furnace TEMPERATURE ( ° C ) Unknown 120-150 175 Unknown TEST TIME ( yrs ) 1/4 2 1-1 / 6 1/2 PREVIOUS MATERIAL 317L 316L 525 / 316L 625 SERVICE LIFE ( yrs ) 2 1/2 Unknown 3-1 / 2 316L P ( 0.010 ) ...
... Boiler Recovery Boiler System Recovery Furnace TEMPERATURE ( ° C ) Unknown 120-150 175 Unknown TEST TIME ( yrs ) 1/4 2 1-1 / 6 1/2 PREVIOUS MATERIAL 317L 316L 525 / 316L 625 SERVICE LIFE ( yrs ) 2 1/2 Unknown 3-1 / 2 316L P ( 0.010 ) ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium