Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 43
Page 193
... behaviour and the sinusoidal waveform leads to a corrosion - fatigue type behaviour with a rapid increase of the growth rate followed by a plateau . The effects of waveform have already been examined by Cullen et al / 14 / and by ...
... behaviour and the sinusoidal waveform leads to a corrosion - fatigue type behaviour with a rapid increase of the growth rate followed by a plateau . The effects of waveform have already been examined by Cullen et al / 14 / and by ...
Page 406
... behaviour could be related to selective anodic dissolution of the active surface followed by local enrichment of the noble alloying element , / 15 , 16 / being probably Cu . During the exposure to the 1NH2SO4 environment surface ...
... behaviour could be related to selective anodic dissolution of the active surface followed by local enrichment of the noble alloying element , / 15 , 16 / being probably Cu . During the exposure to the 1NH2SO4 environment surface ...
Page 408
... behaviour is significantly changed by increasing the Ni content . This behaviour can be related to the enhanced passivation processes taking place due to the enrichment of the surface with Ni . Higher Ni content on the surface of the ...
... behaviour is significantly changed by increasing the Ni content . This behaviour can be related to the enhanced passivation processes taking place due to the enrichment of the surface with Ni . Higher Ni content on the surface of the ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium