Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 53
Page 254
... anodic and cathodic areas . This mechanism is consistent with the ability of polyphosphates to become strongly adsorbed on iron , but implies that at higher con- centrations of the inhibitor an increase followed by a decrease in ...
... anodic and cathodic areas . This mechanism is consistent with the ability of polyphosphates to become strongly adsorbed on iron , but implies that at higher con- centrations of the inhibitor an increase followed by a decrease in ...
Page 266
4. INHIBITOR MIXTURES Mild Steel in Cooling Water Systems 4.1 . Anodic and Cathodic Inhibitors Some inhibitors retard the cathodic reaction while others the anodic reaction . Oxidising inhibitors and orthophosphates are considered anodic ...
4. INHIBITOR MIXTURES Mild Steel in Cooling Water Systems 4.1 . Anodic and Cathodic Inhibitors Some inhibitors retard the cathodic reaction while others the anodic reaction . Oxidising inhibitors and orthophosphates are considered anodic ...
Page 218
... anodic areas as possible . On the other hand , galvanic coupling of the metal structure with sacrificial anodes does not eliminate the corrosion process completely ; it only helps in reducing the activity of the anodic areas appreciably ...
... anodic areas as possible . On the other hand , galvanic coupling of the metal structure with sacrificial anodes does not eliminate the corrosion process completely ; it only helps in reducing the activity of the anodic areas appreciably ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium