Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 40
Page 243
... adsorbed as a monolayer . A number of other studies / 22 , 23 / used radioactive tracing methods and concluded that chromate is adsorbed in multi- layers . Nitrite is considered / 14 / to be more strongly adsorbed than chromate , and ...
... adsorbed as a monolayer . A number of other studies / 22 , 23 / used radioactive tracing methods and concluded that chromate is adsorbed in multi- layers . Nitrite is considered / 14 / to be more strongly adsorbed than chromate , and ...
Page 258
... ADSORPTION INHIBITORS The chemical compounds which belong to this group of inhibitors are believed to inhibit mainly by becoming adsorbed on the metal surface . Adsorption of the inhibitors depends on the potential of the immersed metal ...
... ADSORPTION INHIBITORS The chemical compounds which belong to this group of inhibitors are believed to inhibit mainly by becoming adsorbed on the metal surface . Adsorption of the inhibitors depends on the potential of the immersed metal ...
Page 98
... adsorbed / 29 / . The mechanism of suppression of anodic processes by an inhibitor , according to Timashev / 30 / , is due to modification at the electron structure of the inhibitor molecules and of metal surface during adsorption and ...
... adsorbed / 29 / . The mechanism of suppression of anodic processes by an inhibitor , according to Timashev / 30 / , is due to modification at the electron structure of the inhibitor molecules and of metal surface during adsorption and ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium