Corrosion Reviews, Volume 6, Issues 2-7Scientific Publications Division, Freund Publishing House, 1985 |
From inside the book
Results 1-3 of 29
Page 170
... NaCl whilst Figure 25 shows similar results for a solution 0.1 M NaCl . The important potentials are summarized in Table 3.12 . Unimplanted 04 0.8 1.2 POTENTIAL V ( sce ) SI 40 KeV , 4.1018 cm2 -6 -Or 04 0.8 1.2 POTENTIAL V ( sce ) LOG ...
... NaCl whilst Figure 25 shows similar results for a solution 0.1 M NaCl . The important potentials are summarized in Table 3.12 . Unimplanted 04 0.8 1.2 POTENTIAL V ( sce ) SI 40 KeV , 4.1018 cm2 -6 -Or 04 0.8 1.2 POTENTIAL V ( sce ) LOG ...
Page 311
... NaCl , H2S 190 psia 400 NC NC 25 % NaCl , 90 % CO2 + 10 % H2S 75 psig 500 NC NC 25 % NaCl + 90 % CO2 + 10 % H2S 75 psig 400 NC NC 25 % NaCl + .5 % CH3COOH + H2S 75 psig 350 NC NC 25 % NaCl , O2 400 NC NC NC Boiling MgCh 309 C NC 20 ...
... NaCl , H2S 190 psia 400 NC NC 25 % NaCl , 90 % CO2 + 10 % H2S 75 psig 500 NC NC 25 % NaCl + 90 % CO2 + 10 % H2S 75 psig 400 NC NC 25 % NaCl + .5 % CH3COOH + H2S 75 psig 350 NC NC 25 % NaCl , O2 400 NC NC NC Boiling MgCh 309 C NC 20 ...
Page 186
FeCl3 NaCl + HC1 NaCl + HC1 Wicking Potentio Alloy RT Pit . Temp . Crevice Temp . Effect * Dynamic Table 1. Alloy ranking from laboratory tests ( scale 1 to 10 ) . Average Ranking C - 276 1 1 1 1 1 1.0 625 2 2 3 2 1 2.0 G - 3 2 3 3 2 2 ...
FeCl3 NaCl + HC1 NaCl + HC1 Wicking Potentio Alloy RT Pit . Temp . Crevice Temp . Effect * Dynamic Table 1. Alloy ranking from laboratory tests ( scale 1 to 10 ) . Average Ranking C - 276 1 1 1 1 1 1.0 625 2 2 3 2 1 2.0 G - 3 2 3 3 2 2 ...
Contents
H Craig and R N Parkins | 123 |
Some Studies of Ion Implantation in the Fields of Corrosion and Stress | 126 |
Corrosion Fatigue in Pressurized Water Reactors | 183 |
Copyright | |
47 other sections not shown
Other editions - View all
Common terms and phrases
acid adsorbed aluminium analysis anodic application Artificial Intelligence austenitic cathodic cathodic protection chemical engineering chloride ion chromate composition compounds concentration containing CorDorCD Corrosion Control corrosion fatigue corrosion films Corrosion of Hastelloy corrosion rates corrosion resistance crack growth current density deposits effect electrochemical electron environments evaluation example expert system factors films formed Hastelloy Hastelloy alloy heat exchangers HNO3 implanted increase industry inhibition inhibitor interface ion implantation iron Israel JKTK knowledge base layer mechanism metal surface Metallurgy mild steel molybdenum MYCIN NaCl oxide oxide film oxygen paint passive phosphate pitting corrosion plant plating polarization curves potential primer problems Prof properties protection reduced rules slurry sodium molybdate solution specimens stainless steel stress corrosion cracking structure substrate sulfuric acid Table techniques Technology temperature titanium tube unimplanted values water path welding zinc zirconium