ABSTRACT The corrosion of iron , chromium , nickel and number of their binary and ternary alloys in zinc vapor at 650 C was studied . Auger spectroscopy and X - ray diffraction were used to clarify the mechanism of corrosion .
ABSTRACT The corrosion of iron , chromium , nickel and number of their binary and ternary alloys in zinc vapor at 650 C was studied . Auger spectroscopy and X - ray diffraction were used to clarify the mechanism of corrosion .
Page 392
Liquid zinc has been observed to embrittle aluminum , iron and magnesium / 2 / . The present study was undertaken because only scarce data were found in the literature on high temperature corrosion caused by zinc vapor / 3 / .
Liquid zinc has been observed to embrittle aluminum , iron and magnesium / 2 / . The present study was undertaken because only scarce data were found in the literature on high temperature corrosion caused by zinc vapor / 3 / .
Page 399
When a binary alloy AB is exposed to zinc vapors , the concentration profiles are expected to look like Fig . 13. It was assumed that element A oxidizes at a much faster rate than element B , and that the diffusion coefficient of this ...
When a binary alloy AB is exposed to zinc vapors , the concentration profiles are expected to look like Fig . 13. It was assumed that element A oxidizes at a much faster rate than element B , and that the diffusion coefficient of this ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc