Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 81
Page 245
the internal boiler surface and prevent iron oxide deposition on the heat transfer surface . In the course of our continued research , we have found that acrylic acid / acrylamide copolymers outperform homo- polymers with respect to ...
the internal boiler surface and prevent iron oxide deposition on the heat transfer surface . In the course of our continued research , we have found that acrylic acid / acrylamide copolymers outperform homo- polymers with respect to ...
Page 40
... surfaces , rather than rough flaking surfaces which provide an uneven base for attachment . Because iron immersed in seawater quickly develops a rough surface of iron oxide , as opposed to immersed stainless steel , fouling tends to be ...
... surfaces , rather than rough flaking surfaces which provide an uneven base for attachment . Because iron immersed in seawater quickly develops a rough surface of iron oxide , as opposed to immersed stainless steel , fouling tends to be ...
Page 48
... surface under the tubercle and the well aerated surface outside the tubercle . Consequently , metal goes into solution at the anodic areas of low oxygen concentration under the tubercle . The gross morphology of this Occurrence is seen ...
... surface under the tubercle and the well aerated surface outside the tubercle . Consequently , metal goes into solution at the anodic areas of low oxygen concentration under the tubercle . The gross morphology of this Occurrence is seen ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc