The main problems due to the inhibitor concern the homogeneous distribution in the solution and its chemical stability during the cleaning operation . When a compound is unstable , its decay produces other products which do not always ...
The main problems due to the inhibitor concern the homogeneous distribution in the solution and its chemical stability during the cleaning operation . When a compound is unstable , its decay produces other products which do not always ...
Page 258
To confirm this observation some tests were carried out on ARMCO iron plates , using a solution containing 50g / l of HCl and inhibited with 3cm3 / 1 of commercial product BORG P16 at 75 ° C . When no ferric ions were present ...
To confirm this observation some tests were carried out on ARMCO iron plates , using a solution containing 50g / l of HCl and inhibited with 3cm3 / 1 of commercial product BORG P16 at 75 ° C . When no ferric ions were present ...
Page 381
OH Ox Fe 203 A. Chemical Cleaning Solutions +2 + 2H2O Sources : W.E. Bornak , The Chemistry of Iron and Its Corrosion ... Oxidizing ammonium citrate solution , containing 0.3 % citric acid , 0.2 % NH3 and 0.26 % , NaBrO3 , solution . 3.
OH Ox Fe 203 A. Chemical Cleaning Solutions +2 + 2H2O Sources : W.E. Bornak , The Chemistry of Iron and Its Corrosion ... Oxidizing ammonium citrate solution , containing 0.3 % citric acid , 0.2 % NH3 and 0.26 % , NaBrO3 , solution . 3.
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc