and Beatriz del Amo The different vehicles had the following values : Rosin / phenolic varnish ratio , by weight Residual binder acidity , mg KOH.g - 1 140 These results are consistent with the WW rosin content in each vehicle .
and Beatriz del Amo The different vehicles had the following values : Rosin / phenolic varnish ratio , by weight Residual binder acidity , mg KOH.g - 1 140 These results are consistent with the WW rosin content in each vehicle .
Page 127
Paint film solubility diminishes by reduction of the quantity of uncombined rosin . In sample 2 , with 3 and 12 hours dispersion , final values of 62.2 and 48.0 mg KOH.g " were obtained . The results show that products formulated with ...
Paint film solubility diminishes by reduction of the quantity of uncombined rosin . In sample 2 , with 3 and 12 hours dispersion , final values of 62.2 and 48.0 mg KOH.g " were obtained . The results show that products formulated with ...
Page 148
Red cuprous oxide Tributyl tin fluoride Triphenyl tin fluoride * Zinc oxide Natural calcium carbonate WW rosin ( gum rosin ) Vinyl resin * : Tricresyl phosphate Additives * Solvents and thinners ** Paint *** Antifouling Paints for Ships ...
Red cuprous oxide Tributyl tin fluoride Triphenyl tin fluoride * Zinc oxide Natural calcium carbonate WW rosin ( gum rosin ) Vinyl resin * : Tricresyl phosphate Additives * Solvents and thinners ** Paint *** Antifouling Paints for Ships ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc