In this situation , the metal is attacked by a metabolic byproduct of bacteria , such as hydrogen sulfide , produced by sulfate - reducing bacteria present in the soil 19 , 49 and discussed earlier in this enquiry .
In this situation , the metal is attacked by a metabolic byproduct of bacteria , such as hydrogen sulfide , produced by sulfate - reducing bacteria present in the soil 19 , 49 and discussed earlier in this enquiry .
Page 120
Present state of understanding of the anaerobic corrosion of iron by SRB When the present state of understanding of the microbial corrosion of iron by SRB is taken into account a bioelectrochemical Interpretation of the passivity ...
Present state of understanding of the anaerobic corrosion of iron by SRB When the present state of understanding of the microbial corrosion of iron by SRB is taken into account a bioelectrochemical Interpretation of the passivity ...
Page 270
According to the present results , the protective characteristics of the complex layers that were formed on 70/30 copper - nickel alloy surface could be altered by the microbial adhesion on the metal surface .
According to the present results , the protective characteristics of the complex layers that were formed on 70/30 copper - nickel alloy surface could be altered by the microbial adhesion on the metal surface .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc