Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 92
Page 79
... PAINT Two techniques are applied for derusting and removal of old paint : blast cleaning and chemical cleaning . Statkraft has tested both , chemical paint removers and rust removers . The paint remover tested is based on methylene ...
... PAINT Two techniques are applied for derusting and removal of old paint : blast cleaning and chemical cleaning . Statkraft has tested both , chemical paint removers and rust removers . The paint remover tested is based on methylene ...
Page 80
... PAINT APPLICATION After the cleaning , the penstock was painted inside with four coats of coal - tar paint to a total , dry film thickness of 300 microns . ( Fig . 5 ) . After two years in use an inspection took place and it was found ...
... PAINT APPLICATION After the cleaning , the penstock was painted inside with four coats of coal - tar paint to a total , dry film thickness of 300 microns . ( Fig . 5 ) . After two years in use an inspection took place and it was found ...
Page 120
Antifouling Paints for Ships , Offshore Platforms , and Power Stations – A Review . To obtain an efficient antifouling paint it is necessary to use a correct formulation and the different stages of the manufacture process must be ...
Antifouling Paints for Ships , Offshore Platforms , and Power Stations – A Review . To obtain an efficient antifouling paint it is necessary to use a correct formulation and the different stages of the manufacture process must be ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc