The purity , expressed as cuprous oxide , was 99.84 per cent . During storage and previous to paint preparation , the composition of cuprous oxide had changed with an increase of the amount of Cu ° and Cu ( II ) .
The purity , expressed as cuprous oxide , was 99.84 per cent . During storage and previous to paint preparation , the composition of cuprous oxide had changed with an increase of the amount of Cu ° and Cu ( II ) .
Page 247
Linear oxide growth with the square root of time is also indicative of passive , protective film formation / 12 / . The graph shows that the rate of formation of a passive film is diffusion controlled only for a short time ( < 20 hours ) ...
Linear oxide growth with the square root of time is also indicative of passive , protective film formation / 12 / . The graph shows that the rate of formation of a passive film is diffusion controlled only for a short time ( < 20 hours ) ...
Page 364
Appearance EDS ( 4 ) Results : ( Peak Ratio / Ca ) Thin , loose , airformed brown iron oxide . Red - brown magnetite & metallic Cu , and Ni . Red color ; metallic Cu . Clean Steel Clean steel , Cu spots thin iron oxide . and R.
Appearance EDS ( 4 ) Results : ( Peak Ratio / Ca ) Thin , loose , airformed brown iron oxide . Red - brown magnetite & metallic Cu , and Ni . Red color ; metallic Cu . Clean Steel Clean steel , Cu spots thin iron oxide . and R.
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc