... operation of a steam generator , it is practically impossible to attain optimum protection by passivation through the formation of a thin , compact magnetite layer . When the steam generator is in operation , the thickness of the oxide ...
... operation of a steam generator , it is practically impossible to attain optimum protection by passivation through the formation of a thin , compact magnetite layer . When the steam generator is in operation , the thickness of the oxide ...
Page 40
... operation . In most cases a product is specific for a certain environment and cannot be employed for all types of acid . If it is used with acids that have not been recommended by the manufacturer , it can lose its inhibitor ...
... operation . In most cases a product is specific for a certain environment and cannot be employed for all types of acid . If it is used with acids that have not been recommended by the manufacturer , it can lose its inhibitor ...
Page 361
... operation . a . The unit was cleaned in a three - stage operation using : Inhibited hydrochloric acid , to dissolve scale and corrosion products . b . An oxidixing , ammoniacal solution for metallic copper removal , and A passivating ...
... operation . a . The unit was cleaned in a three - stage operation using : Inhibited hydrochloric acid , to dissolve scale and corrosion products . b . An oxidixing , ammoniacal solution for metallic copper removal , and A passivating ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc