Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 5
Page 26
... molybdenum ( SA - 213 T22 ) . It had been removed from a 2500 psi ( 17.2 MPa ) , base - loaded utility boiler whose initial start - up was in 1979. The first failure of this type occurred in August 1980. A second failure occurred in ...
... molybdenum ( SA - 213 T22 ) . It had been removed from a 2500 psi ( 17.2 MPa ) , base - loaded utility boiler whose initial start - up was in 1979. The first failure of this type occurred in August 1980. A second failure occurred in ...
Page 227
... molybdenum steel A217-55 WC6 0.20 C max , 1.25 Cr , 0.50 Mo 1050 Cast chromium - molybdenum steel A217-55 WC9 0.18 C max , 1.25 Cr , 0.50 Mo 1050 Cast carbon - molybdenum steel ( a ) A217-55 WCI 0.25 C max , 0.50 Mo 850 Forged carbon - ...
... molybdenum steel A217-55 WC6 0.20 C max , 1.25 Cr , 0.50 Mo 1050 Cast chromium - molybdenum steel A217-55 WC9 0.18 C max , 1.25 Cr , 0.50 Mo 1050 Cast carbon - molybdenum steel ( a ) A217-55 WCI 0.25 C max , 0.50 Mo 850 Forged carbon - ...
Page 228
... molybdenum steel pipe A335-55T P1 0.15 C , 0.50 Mo 850 1.25 % chromium - molybdenum steel pipe A335-55T P11 0.15 C max , 1.25 Cr , 0.50 Mo 1050 1 % chromium - molybdenum steel pipe A335-55T P12 0.15 C max , 1.00 Cr , 0.50 Mo 1000 2.25 ...
... molybdenum steel pipe A335-55T P1 0.15 C , 0.50 Mo 850 1.25 % chromium - molybdenum steel pipe A335-55T P11 0.15 C max , 1.25 Cr , 0.50 Mo 1050 1 % chromium - molybdenum steel pipe A335-55T P12 0.15 C max , 1.00 Cr , 0.50 Mo 1000 2.25 ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc