Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 36
Page 114
... mild steel . Localized corrosion measurements such as pitting potential values ( E_ ) , repassivation potentials ( E_ ) , induction times for pitting , kinetics of pit growth , plt density and morphology of pits were employed . The ...
... mild steel . Localized corrosion measurements such as pitting potential values ( E_ ) , repassivation potentials ( E_ ) , induction times for pitting , kinetics of pit growth , plt density and morphology of pits were employed . The ...
Page 117
... steel has been recently published ( Newman et al . , 1986 ) confirming these effects of sulphur compounds other than ... mild steel by sulphide anions has already been reported ( Acosta et al . , 1984 ) . A typical experiment to ...
... steel has been recently published ( Newman et al . , 1986 ) confirming these effects of sulphur compounds other than ... mild steel by sulphide anions has already been reported ( Acosta et al . , 1984 ) . A typical experiment to ...
Page 125
... metal surface after 24 hrs . of incubating mild steel samples in a laboratory batch fermentor Innoculated with Vibria alginolyticus . After colony removal the metal underneath showed localized areas of attack where generalized corrosion ...
... metal surface after 24 hrs . of incubating mild steel samples in a laboratory batch fermentor Innoculated with Vibria alginolyticus . After colony removal the metal underneath showed localized areas of attack where generalized corrosion ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc