Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 82
Page 178
... layers , together with pitting on the inner layers . In marine environments , corrosion is predominantly on the steel core , due to the galvanic process between the innermost aluminum layer and the galvanized steel , together with ...
... layers , together with pitting on the inner layers . In marine environments , corrosion is predominantly on the steel core , due to the galvanic process between the innermost aluminum layer and the galvanized steel , together with ...
Page 399
... layer . When the concentration of A drops appreciably , B increases but zinc also drops because B did not form and intermetallic compound with zinc . Examination of the Auger profiles ( Figs . 4-11 ) leads to the following conclusions ...
... layer . When the concentration of A drops appreciably , B increases but zinc also drops because B did not form and intermetallic compound with zinc . Examination of the Auger profiles ( Figs . 4-11 ) leads to the following conclusions ...
Page 289
... layer is mainly Cu2 ( OH ) 3Cl with some Cu2 ) and Cu2S particles . The inner layer was attributed to Cu20 doped with Ni , Fe , S and Cl / 4 / . After a few days of immersion , corrosion products layers are formed by an adherent continuous ...
... layer is mainly Cu2 ( OH ) 3Cl with some Cu2 ) and Cu2S particles . The inner layer was attributed to Cu20 doped with Ni , Fe , S and Cl / 4 / . After a few days of immersion , corrosion products layers are formed by an adherent continuous ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc