From inside the book
Results 1-3 of 34
Page 166
Cathodic protection was provided when the structures were installed . Thirty pound ( 13.6kg ) zinc anodes were installed in the lower resistivity soils and 20 pound ( 9.1 kg ) high potential anodes were installed elsewhere . Fig . 8 .
Cathodic protection was provided when the structures were installed . Thirty pound ( 13.6kg ) zinc anodes were installed in the lower resistivity soils and 20 pound ( 9.1 kg ) high potential anodes were installed elsewhere . Fig . 8 .
Page 169
Install cathodic protection as soon as practicable in order to preserve as much galvanizing as possible . 2. Remove all copper grounding ... Anodes are to be installed in accordance with Figure 11 . 5 . 6 . Install anodes on pipe piling ...
Install cathodic protection as soon as practicable in order to preserve as much galvanizing as possible . 2. Remove all copper grounding ... Anodes are to be installed in accordance with Figure 11 . 5 . 6 . Install anodes on pipe piling ...
Page 170
Install first two anodes on diagonal guys . 2. ... If soil resistivity is 10K OHM - CM or less , install a zinc anode . ... Record structure - to - soil potentials on all guys and center point after all anodes are installed . 1.
Install first two anodes on diagonal guys . 2. ... If soil resistivity is 10K OHM - CM or less , install a zinc anode . ... Record structure - to - soil potentials on all guys and center point after all anodes are installed . 1.
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc