Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 24
Page 44
... impedance modulus at 2 Hz . The tests for the weight loss and the impedance measurements at 2 Hz lasted six hours on an average and were performed with the same sample . The corrosion current density Table : Electrochemical parameters ...
... impedance modulus at 2 Hz . The tests for the weight loss and the impedance measurements at 2 Hz lasted six hours on an average and were performed with the same sample . The corrosion current density Table : Electrochemical parameters ...
Page 56
... impedance modulus at 2 Hz . This is because the function | Z | = | Z ( t ) | is almost constant in time and the function I = A / IZI , where the parameter A is determined by the best - fitting of the experimental results , reproduces ...
... impedance modulus at 2 Hz . This is because the function | Z | = | Z ( t ) | is almost constant in time and the function I = A / IZI , where the parameter A is determined by the best - fitting of the experimental results , reproduces ...
Page 143
... 6. REFERENCES WILKES 162 Condenser Tubes Coatings ABSTRACT Long term testing to evaluate the 143 TABLE OF CONTENTS Page Characterization of Condenser Tubes Coatings Electrochemical Impedance A Colombo, G Rocchini and P Spinelli 143.
... 6. REFERENCES WILKES 162 Condenser Tubes Coatings ABSTRACT Long term testing to evaluate the 143 TABLE OF CONTENTS Page Characterization of Condenser Tubes Coatings Electrochemical Impedance A Colombo, G Rocchini and P Spinelli 143.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc