... hydrazine . Catalyzed hydrazine out - performs hydrazine and might be preferred when catalyzed sulfite cannot be used . Data from a Midwest Utility confirms that , under field conditions , catalyzed hydrazine out - performed hydrazine ...
... hydrazine . Catalyzed hydrazine out - performs hydrazine and might be preferred when catalyzed sulfite cannot be used . Data from a Midwest Utility confirms that , under field conditions , catalyzed hydrazine out - performed hydrazine ...
Page 4
... hydrazine over plain hydrazine and in relation to catalyzed sulfite . Another study was conducted to compare oxygen scavenging performance of the three hydrazines . The results are presented in Figure 2 . 8 ง © ( 20 Oxygen ( ppm ♡ 2 1 ...
... hydrazine over plain hydrazine and in relation to catalyzed sulfite . Another study was conducted to compare oxygen scavenging performance of the three hydrazines . The results are presented in Figure 2 . 8 ง © ( 20 Oxygen ( ppm ♡ 2 1 ...
Page 8
... Hydrazine Figure Month 2-3 Month 4-8 Month 1-8 Hydrazine Month 3-4 Carbohydre.zide · Month 8-0 Catalyzed Hydrazine Fig . 5 This was a very high pressure system ( 2300 psig ) so the organic- catalyzed hydrazine was evaluated rather than ...
... Hydrazine Figure Month 2-3 Month 4-8 Month 1-8 Hydrazine Month 3-4 Carbohydre.zide · Month 8-0 Catalyzed Hydrazine Fig . 5 This was a very high pressure system ( 2300 psig ) so the organic- catalyzed hydrazine was evaluated rather than ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc