Page 310
18 ) for Admiralty brass , in contact with mud , but with different surface conditions , present higher anodic currents . The result of dissolution at a controlled potential indicates that the Zn amount detected at 200 mV is three times ...
18 ) for Admiralty brass , in contact with mud , but with different surface conditions , present higher anodic currents . The result of dissolution at a controlled potential indicates that the Zn amount detected at 200 mV is three times ...
Page 285
EDXA of the outer layers revealed the presence of S and higher levels of Fe than those of the base metal . At the bottom of the cracks higher levels of Cl than those found in the film were detected / 14 / . 70/30 copper - nickel samples ...
EDXA of the outer layers revealed the presence of S and higher levels of Fe than those of the base metal . At the bottom of the cracks higher levels of Cl than those found in the film were detected / 14 / . 70/30 copper - nickel samples ...
Page 362
1 : Electrolytic cell for electrochemical temperatures higher than room temperature . the SOFTCOR - DC - PSI Program out . measurements and kept the temperature constant throughout the test . The temperature regulation was of the on ...
1 : Electrolytic cell for electrochemical temperatures higher than room temperature . the SOFTCOR - DC - PSI Program out . measurements and kept the temperature constant throughout the test . The temperature regulation was of the on ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc