Page 178
However , in saline or highly polluted environments , this oxide layer may become unstable , allowing rapid attack of the metal . Corrosion occurs by pitting , and is directly related to the concentration of pollutants , time of wetness ...
However , in saline or highly polluted environments , this oxide layer may become unstable , allowing rapid attack of the metal . Corrosion occurs by pitting , and is directly related to the concentration of pollutants , time of wetness ...
Page 404
(021) 263.0930 - 263.9833 Corrosion and the Environment Corrosio i Medi Ambient Proceedings of the 2nd Conference on ... contamination of waters, atmospheric corrosion, and corrosion in various natural and industrial environments.
(021) 263.0930 - 263.9833 Corrosion and the Environment Corrosio i Medi Ambient Proceedings of the 2nd Conference on ... contamination of waters, atmospheric corrosion, and corrosion in various natural and industrial environments.
Page 141
... of microbial corrosion and in assessing the corrosivity of a wide range of terrestrial and marine environments . ... mild steel and AISI 304 stainless steel by blue - green and red algae in an estuarine environment in India ; steel ...
... of microbial corrosion and in assessing the corrosivity of a wide range of terrestrial and marine environments . ... mild steel and AISI 304 stainless steel by blue - green and red algae in an estuarine environment in India ; steel ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc