Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 32
Page 395
... depth ( mm ) Fig . 7. Auger depth profile of corroded Invar . the interface zone , which comprises both metal and zinc , will be arranged in a manner that the outermost layer will be the richest in zinc , while the innermost layer the ...
... depth ( mm ) Fig . 7. Auger depth profile of corroded Invar . the interface zone , which comprises both metal and zinc , will be arranged in a manner that the outermost layer will be the richest in zinc , while the innermost layer the ...
Page 396
... depth ( nm ) Ni En Auger depth profile of corroded SS 410 . Cr 800 1600 1400 3200 depth ( mm ) Fig . 9. Auger depth profile of corroded Nimonic . should be noted that the phase rule does not preclude the existence of transition zones ...
... depth ( nm ) Ni En Auger depth profile of corroded SS 410 . Cr 800 1600 1400 3200 depth ( mm ) Fig . 9. Auger depth profile of corroded Nimonic . should be noted that the phase rule does not preclude the existence of transition zones ...
Page 397
... depth profile of corroded Inconel . N : tn Fe Cr 400 800 1200 1600 depth ( mm ) Fig . 11. Auger depth profile of corroded SS 310 . When a pure element A is exposed to zinc vapor , the resulting depth profiles in the interfacial region ...
... depth profile of corroded Inconel . N : tn Fe Cr 400 800 1200 1600 depth ( mm ) Fig . 11. Auger depth profile of corroded SS 310 . When a pure element A is exposed to zinc vapor , the resulting depth profiles in the interfacial region ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc