Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 22
Page 106
... cuprous oxide ) by more economical substances , but maintaining adequate solids volume and satisfactory antifouling protection . Calcium carbonate ( CaCO3 ) is usually employed in antifouling paints formulations . This extender ...
... cuprous oxide ) by more economical substances , but maintaining adequate solids volume and satisfactory antifouling protection . Calcium carbonate ( CaCO3 ) is usually employed in antifouling paints formulations . This extender ...
Page 120
... cuprous oxide , was 99.84 per cent . During storage and previous to paint preparation , the composition of cuprous oxide had changed with an increase of the amount of Cu ° and Cu ( II ) . Within 10 days the metallic copper reached a ...
... cuprous oxide , was 99.84 per cent . During storage and previous to paint preparation , the composition of cuprous oxide had changed with an increase of the amount of Cu ° and Cu ( II ) . Within 10 days the metallic copper reached a ...
Page 126
... oxidation of cuprous oxide . As was observed during extender dispersion , increased cuprous oxide content in the paint led to increased reaction with the resinic acids , demonstrated by the residual acidity . For example , in paints 10 ...
... oxidation of cuprous oxide . As was observed during extender dispersion , increased cuprous oxide content in the paint led to increased reaction with the resinic acids , demonstrated by the residual acidity . For example , in paints 10 ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc