Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 26
Page 24
... crack ( Figure 17 ) . Lead Channeling Along Corrosion Fatigue Crack Fig . 17 500x Lead running from tip of corrosion fatigue crack backscatter electron image . Figure 18 is an EDS spectrum of the material within the cracks showing the ...
... crack ( Figure 17 ) . Lead Channeling Along Corrosion Fatigue Crack Fig . 17 500x Lead running from tip of corrosion fatigue crack backscatter electron image . Figure 18 is an EDS spectrum of the material within the cracks showing the ...
Page 28
... crack . Examination of the rupture face reveals that it possesses the same curvature as the crack over the entire length of the rupture ( Figure 21 ) . Fig . 21 The smooth area of the face corresponds exactly with the extent of the ...
... crack . Examination of the rupture face reveals that it possesses the same curvature as the crack over the entire length of the rupture ( Figure 21 ) . Fig . 21 The smooth area of the face corresponds exactly with the extent of the ...
Page 30
... crack path . 20X : Nital Etch . Flow of microstructure following crack path . 50X : Nital Etch . Flow of microstructure and inclusions along crack path . 100X. 30 Vol . 8 , Nos . 1 & 2 , 1988 Two Case Histories of Unusual Brittle.
... crack path . 20X : Nital Etch . Flow of microstructure following crack path . 50X : Nital Etch . Flow of microstructure and inclusions along crack path . 100X. 30 Vol . 8 , Nos . 1 & 2 , 1988 Two Case Histories of Unusual Brittle.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc