Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 69
Page 26
... containing antimony . Antimony is known to cause liquid metal embrittlement of carbon steel / 5 / . Lead alloys containing 2 % antimony have a pronounced embrittling effect on carbon steel at metal temperatures above 500 ° ` F / 6 / . 2 ...
... containing antimony . Antimony is known to cause liquid metal embrittlement of carbon steel / 5 / . Lead alloys containing 2 % antimony have a pronounced embrittling effect on carbon steel at metal temperatures above 500 ° ` F / 6 / . 2 ...
Page 381
... containing 0.3 % NH4HF2 and 0.2 % Rodine 213 inhibitor ( Film - forming amine - type inhibitor ) ( Amchem Products , USA ) . 2. Copper Removal Metallic copper complexing and removal . Oxidizing ammonium citrate solution , containing 0.3 ...
... containing 0.3 % NH4HF2 and 0.2 % Rodine 213 inhibitor ( Film - forming amine - type inhibitor ) ( Amchem Products , USA ) . 2. Copper Removal Metallic copper complexing and removal . Oxidizing ammonium citrate solution , containing 0.3 ...
Page 35
... containing both iron and sulfate - reducing bacteria have also been observed to corrode stainless steel In addition , Gallionella also accumulates manganese and chloride and often , bacterial deposits contain high levels of ferric and ...
... containing both iron and sulfate - reducing bacteria have also been observed to corrode stainless steel In addition , Gallionella also accumulates manganese and chloride and often , bacterial deposits contain high levels of ferric and ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc