Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 57
Page 11
... Conclusion 1.4 . Scanning electron microscope evidence 1.5 . Chemical analysis of shot 2. CASE II - TUBE DEFECT 2.1 . Introduction 2.2 . Visual evidence 21 25 25 26 26 26 2.3 . Metallographic evidence 29 2.4 . Conclusion 3. REFERENCES ...
... Conclusion 1.4 . Scanning electron microscope evidence 1.5 . Chemical analysis of shot 2. CASE II - TUBE DEFECT 2.1 . Introduction 2.2 . Visual evidence 21 25 25 26 26 26 2.3 . Metallographic evidence 29 2.4 . Conclusion 3. REFERENCES ...
Page 25
... Conclusion Based on this evidence , the sequence of events leading to the failure can be established as follows : 1. Boiler tubes were deslagged on - line by the use of shotguns . To facilitate slag removal a new type of copper ...
... Conclusion Based on this evidence , the sequence of events leading to the failure can be established as follows : 1. Boiler tubes were deslagged on - line by the use of shotguns . To facilitate slag removal a new type of copper ...
Page 32
... Conclusion It is apparent that the failure of the ruptured tube was a direct consequence of a massive defect in the tube wall . The defect appears to be an internal lap or seam , possibly associated with remnants of pipe ( internal ...
... Conclusion It is apparent that the failure of the ruptured tube was a direct consequence of a massive defect in the tube wall . The defect appears to be an internal lap or seam , possibly associated with remnants of pipe ( internal ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc