Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 32
Page 89
... binder ) , to the immersion tests ( raft and ships hull , dry film thickness , immersion time , neutralization chemical reactions between sea water cations and remaining acidic components of binder ) and , finally , characteristics of ...
... binder ) , to the immersion tests ( raft and ships hull , dry film thickness , immersion time , neutralization chemical reactions between sea water cations and remaining acidic components of binder ) and , finally , characteristics of ...
Page 126
... binder was observed ( Table VI ) , as a result of the neutralization of the calcium carbonate incorporated , by binder acid components . For example , in paints 2 and 6 ( 19 and 32 g per cent of calcium carbonate , respectively ) , with ...
... binder was observed ( Table VI ) , as a result of the neutralization of the calcium carbonate incorporated , by binder acid components . For example , in paints 2 and 6 ( 19 and 32 g per cent of calcium carbonate , respectively ) , with ...
Page 130
... binder with the 2/1 rosin / chlorinated rubber ratio , the content of resinic acids decreased rapidly in the film surface and more slowly in the inner layers . Initial content was 23.8 % , expressed as abietic acid on binder solids ...
... binder with the 2/1 rosin / chlorinated rubber ratio , the content of resinic acids decreased rapidly in the film surface and more slowly in the inner layers . Initial content was 23.8 % , expressed as abietic acid on binder solids ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc