Corrosion Reviews, Volumes 8-9Scientific Publications Division, Freund Publishing House, 1988 |
From inside the book
Results 1-3 of 62
Page 295
... Anodic curves for Cu - Ni 70/30 . corr anodic respect to the Ecorr in the polished condition , but it moves to 180 mV respect to the E in the aged condition . In the presence of sulphide the pitting potential for each condition is ...
... Anodic curves for Cu - Ni 70/30 . corr anodic respect to the Ecorr in the polished condition , but it moves to 180 mV respect to the E in the aged condition . In the presence of sulphide the pitting potential for each condition is ...
Page 322
... anodic curves in natural seawater . The ferrous ion was supplied by a FeSO47H2O solution , described above . The different conditions tested were : 1. Polished , as before 2. Aged , as before 3. Fe + 2 treated samples : samples ...
... anodic curves in natural seawater . The ferrous ion was supplied by a FeSO47H2O solution , described above . The different conditions tested were : 1. Polished , as before 2. Aged , as before 3. Fe + 2 treated samples : samples ...
Page 55
... anodic depolarization under aerobic conditions , hence promoting corrosion . Corrosion was also stimulated , to a smaller degree , by cathodic depolarization caused by metabolites formed by film - forming microorganisms . Anodic ...
... anodic depolarization under aerobic conditions , hence promoting corrosion . Corrosion was also stimulated , to a smaller degree , by cathodic depolarization caused by metabolites formed by film - forming microorganisms . Anodic ...
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
59 other sections not shown
Other editions - View all
Common terms and phrases
acid cleaning alloy aluminum anaerobic anodic Antifouling Paints Association of Corrosion Beatriz del Amo behaviour binder biocorrosion Biodeterioration biofilm Biofouling Boiler Tubes calcium carbon steel cathodic protection chemical chloride clad plate coating concentration condensate conductors copper Corrosion Engineers corrosion products corrosion rate crack cupronickels cuprous oxide deposits Desulfovibrio dispersion dissolution rate effect electrical Electrical Conductors electrochemical electrode environment evaluation experimental Figure film fouling fuel hydrazine hydrogen sulfide immersion industrial inhibitor installed internal iron layer magnetite marine materials mechanism metal surface microbial Microbial Corrosion microorganisms mild steel NACE Offshore Platforms organisms oxygen Paints for Ships pigment pipe pitting plant polarization curves polymer potential Power Stations present Proc Puerto Belgrano Rascio reaction resinates resinic acids resistance Review rosin samples sea water seawater soil solubility solution stainless steel steam structure sulfate-reducing bacteria sulphide superheater Table techniques temperature tests Thermal toxicant values welded zinc