Page 38
Inhibitors Used for the Acid Cleaning of Steam Generators M Μ The SOFTCOR - DC - PS1 program performs the determination of the polarization resistance value over the interval [ E - 20 , EM +20 ] mV using the potentiostatic configuration ...
Inhibitors Used for the Acid Cleaning of Steam Generators M Μ The SOFTCOR - DC - PS1 program performs the determination of the polarization resistance value over the interval [ E - 20 , EM +20 ] mV using the potentiostatic configuration ...
Page 39
The second case concerns the cleaning of an once through boiler , performed at 90 ° C using an organic acid solution whose typical composition was : glycolic acid 1.5 % , formic acid 1.5 % , ammonium bifluoride 0.3 % , and a specific ...
The second case concerns the cleaning of an once through boiler , performed at 90 ° C using an organic acid solution whose typical composition was : glycolic acid 1.5 % , formic acid 1.5 % , ammonium bifluoride 0.3 % , and a specific ...
Page 248
The above results show that acrylic acid / acrylamide copolymers are superior to homopolymers based on both their iron dispersion ability and passivation properties . In the all - polymer treatment , the acrylic acid / acrylamide ratio ...
The above results show that acrylic acid / acrylamide copolymers are superior to homopolymers based on both their iron dispersion ability and passivation properties . In the all - polymer treatment , the acrylic acid / acrylamide ratio ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc