INTRODUCTION The problems related to the fixation of marine fouling organisms on substrates submerged in sea water ( commercial or war ships , ports , buoys , offshore platforms , pipelines , power stations refrigerating equipments ...
INTRODUCTION The problems related to the fixation of marine fouling organisms on substrates submerged in sea water ( commercial or war ships , ports , buoys , offshore platforms , pipelines , power stations refrigerating equipments ...
Page 92
Antifouling Paints for Ships , Offshore Platforms , and Power Stations – A Review . pigments or additives soluble in sea water . As the paint is completely removed from the ship hull , a new coat is directly applied after jet water ...
Antifouling Paints for Ships , Offshore Platforms , and Power Stations – A Review . pigments or additives soluble in sea water . As the paint is completely removed from the ship hull , a new coat is directly applied after jet water ...
Page 112
1300 1000700 600 800 Antifouling Paints for Ships , Offshore Platforms , and Power Stations - A Review . 1000 1200 1400 12 hours 24 hours 36 hours 48 hours 1600 1800 2000 BALL VOLUME ( ml ) Dispersion efficiency ( coefficient moment ) ...
1300 1000700 600 800 Antifouling Paints for Ships , Offshore Platforms , and Power Stations - A Review . 1000 1200 1400 12 hours 24 hours 36 hours 48 hours 1600 1800 2000 BALL VOLUME ( ml ) Dispersion efficiency ( coefficient moment ) ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
Electrochemical characterization of some commercial | 36 |
EXPERIMENTAL RESULTS | 44 |
DISCUSSION AND CONCLUSIONS | 51 |
63 other sections not shown
Other editions - View all
Common terms and phrases
acid additional alloy aluminum anodes Antifouling Paints application Association ball behaviour binder boiler Brazil cable calcium carbon carried cent chemical clad cleaning coatings concentration conductors considered construction copper corrosion crack cuprous oxide density determined dispersion dissolution rate effect electrical electrochemical Engineers environments evaluation experimental Figure film fouling galvanized grounding immersion important increase industrial influence inhibitor installed Institute internal layer levels lines materials measurements mechanical metal method mill months necessary obtained Offshore Platforms operation organic oxygen particles performance period pigment plants plate polarization polymer potential Power Stations practical present problems protection recommended removal resinates resistance Review rosin samples sea water Ships shown shows soil solubility solution steel structure surface Table Technology temperature tests toxicant tube units values weight welded zinc