Page 127
Galvanic corrosion at welds From a corrosion point of view it is of great importance that the weld metal is formulated in such a manner that galvanic effects do not arise with the weld metal being the anode since the much smaller ...
Galvanic corrosion at welds From a corrosion point of view it is of great importance that the weld metal is formulated in such a manner that galvanic effects do not arise with the weld metal being the anode since the much smaller ...
Page 128
There was a strong suggestion however that weld corrosion was associated with the volume fraction of FeO / Fe3O4 type precipitates present in weld metals , particularly of the low hydrogen type . Hicks / 169 / discussed the results of ...
There was a strong suggestion however that weld corrosion was associated with the volume fraction of FeO / Fe3O4 type precipitates present in weld metals , particularly of the low hydrogen type . Hicks / 169 / discussed the results of ...
Page 129
ing rate after welding of a C - Mn steel may heavily influence the corrosion susceptibility of the heat affected zone ... finding that the potential of the HAZ was more negative than that of either the weld metal or the base material .
ing rate after welding of a C - Mn steel may heavily influence the corrosion susceptibility of the heat affected zone ... finding that the potential of the HAZ was more negative than that of either the weld metal or the base material .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld