Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 77
Page 53
... tests , although in the tests described this had an effect only at short times , the long term pH being apparently determined by precipitation of Al ( OH ) 3 . Shibu Discussion The preceding outline of techniques for measuring the ...
... tests , although in the tests described this had an effect only at short times , the long term pH being apparently determined by precipitation of Al ( OH ) 3 . Shibu Discussion The preceding outline of techniques for measuring the ...
Page 177
... Tests ( SSRTs ) were carried out on uniaxial tension specimens in high - temperature water systems . In these tests , specimens were slowly elongated in high - purity water that was maintained at a constant temperature and a controlled ...
... Tests ( SSRTs ) were carried out on uniaxial tension specimens in high - temperature water systems . In these tests , specimens were slowly elongated in high - purity water that was maintained at a constant temperature and a controlled ...
Page 182
... tests by H2O2 additions to water in the feed tank . Initially , the feed tank water contained either 0.2 or 8.0 ppm dissolved oxygen for these specific tests . SLOW STRAIN RATE TESTS The SSRT evaluations provided direct information on ...
... tests by H2O2 additions to water in the feed tank . Initially , the feed tank water contained either 0.2 or 8.0 ppm dissolved oxygen for these specific tests . SLOW STRAIN RATE TESTS The SSRT evaluations provided direct information on ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld