Thirty years ago , the possibility of producing improved aluminium alloys by the powder technique was demonstrated ... Such techniques are very attractive due to their lower energy requirements and lower materials losses in comparison ...
Thirty years ago , the possibility of producing improved aluminium alloys by the powder technique was demonstrated ... Such techniques are very attractive due to their lower energy requirements and lower materials losses in comparison ...
Page 4
More than 20 years later , in a Belgian patent , Aquesse / 5 / proposed the use of this technique to increase the lifetime of cutting tools by codeposition of a hard second phase . It was in the early sixties that the need to further ...
More than 20 years later , in a Belgian patent , Aquesse / 5 / proposed the use of this technique to increase the lifetime of cutting tools by codeposition of a hard second phase . It was in the early sixties that the need to further ...
Page 49
Pickering and Frankenthal / 15 / employed a similar technique , i.e. a microprobe reference electrode with a glass capillary drawn to a tip 50 um in diameter , for measuring the potential inside a pit . The microprobe was attached to a ...
Pickering and Frankenthal / 15 / employed a similar technique , i.e. a microprobe reference electrode with a glass capillary drawn to a tip 50 um in diameter , for measuring the potential inside a pit . The microprobe was attached to a ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld