Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 28
Page 113
... studied the anodic dissolution of a mild steel ( composition in weight per cent , C : 0.12 , Mn : 0.51 , Si : 0.28 , S : 0.016 , P : 0.028 ) in a variety of media including deaerated solutions of 10-2 and 10 M NaCl . The polarisation ...
... studied the anodic dissolution of a mild steel ( composition in weight per cent , C : 0.12 , Mn : 0.51 , Si : 0.28 , S : 0.016 , P : 0.028 ) in a variety of media including deaerated solutions of 10-2 and 10 M NaCl . The polarisation ...
Page 100
... studied compositional depth profiles of air - formed oxides on steels by means of lon Scattering Spectroscopy . They showed that the oxygen content diminished continuously , while the concentration of Cr had an initial sharp rise , and ...
... studied compositional depth profiles of air - formed oxides on steels by means of lon Scattering Spectroscopy . They showed that the oxygen content diminished continuously , while the concentration of Cr had an initial sharp rise , and ...
Page 102
... studied were Ni Co Mo Ti Mn ะก Fe 0.2 0.008 bal Kovar 29 17.4 Maraging steel , grade 250 18 8 4.8 0.4 0.03 bal Prior to oxidation , specimens were cleaned in a vapor phase degreaser . Oxidation was carried out in a Degussa DSU steam oven ...
... studied were Ni Co Mo Ti Mn ะก Fe 0.2 0.008 bal Kovar 29 17.4 Maraging steel , grade 250 18 8 4.8 0.4 0.03 bal Prior to oxidation , specimens were cleaned in a vapor phase degreaser . Oxidation was carried out in a Degussa DSU steam oven ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld