Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 82
Page 94
... steels . No noticeable effect on the pH was observed as a result of pH variations in the bulk solution . M. Pourbaix / 35 / obtained pH measurements , using the " Pourbaix " cell for a carbon steel ( unspecified composition ) in ...
... steels . No noticeable effect on the pH was observed as a result of pH variations in the bulk solution . M. Pourbaix / 35 / obtained pH measurements , using the " Pourbaix " cell for a carbon steel ( unspecified composition ) in ...
Page 189
... steel in oxygenated water , neither cyclic potential oscillations nor pitting occurred . Obviously , carbon steel is far more susceptible to pitting in pure water than Type - 304 stainless steel , and with decreasing temperature ...
... steel in oxygenated water , neither cyclic potential oscillations nor pitting occurred . Obviously , carbon steel is far more susceptible to pitting in pure water than Type - 304 stainless steel , and with decreasing temperature ...
Page 219
... steel indicate that stress corrosion is generally a more difficult process in carbon steel . In high - temperature water , it was found that the lower the potential , the less the susceptibility of Type - 304 stainless steel to TGSCC ...
... steel indicate that stress corrosion is generally a more difficult process in carbon steel . In high - temperature water , it was found that the lower the potential , the less the susceptibility of Type - 304 stainless steel to TGSCC ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld