161 , 62 / reported pH values or order 2.5 to 5 in the anode region of an iron macropit formed in artificial sea water under an oxygen atmosphere at 500 psi . The steady state potential ( achieved after 4 days ) in the anodic region was ...
161 , 62 / reported pH values or order 2.5 to 5 in the anode region of an iron macropit formed in artificial sea water under an oxygen atmosphere at 500 psi . The steady state potential ( achieved after 4 days ) in the anodic region was ...
Page 133
Francis did not carry out experiments at potentials more negative than 0.9 V ( SCE ) and thus no corroboration of the increased protectiveness of the film at -1.03 V ( SCE ) reported by Hartt and Wolfson is possible .
Francis did not carry out experiments at potentials more negative than 0.9 V ( SCE ) and thus no corroboration of the increased protectiveness of the film at -1.03 V ( SCE ) reported by Hartt and Wolfson is possible .
Page 146
The pH of the solution in a propagating fatigue crack in structural steel in sea water was reported to be 4 for R = 0.6 , AK = 9.5M Nm and frequency = 0.1 Hz but a value equivalent to the bulk value of 8.2 was measured under fully ...
The pH of the solution in a propagating fatigue crack in structural steel in sea water was reported to be 4 for R = 0.6 , AK = 9.5M Nm and frequency = 0.1 Hz but a value equivalent to the bulk value of 8.2 was measured under fully ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld