Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 74
Page 67
... regions , a tip zone where the cleavage process took place , an inner region or monolayer zone where a first monolayer of oxide was formed on the metal surface and an outer region or multilayer zone where the oxide layer increased in ...
... regions , a tip zone where the cleavage process took place , an inner region or monolayer zone where a first monolayer of oxide was formed on the metal surface and an outer region or multilayer zone where the oxide layer increased in ...
Page 123
... region of elastic straining the change in the anodic current , if any , is very small ( see for example the paper by Despic et al . / 144 / ) . In the region of plastic deformation the change in the anodic current density due to ...
... region of elastic straining the change in the anodic current , if any , is very small ( see for example the paper by Despic et al . / 144 / ) . In the region of plastic deformation the change in the anodic current density due to ...
Page 126
... region of passive oxide formation the relative increase in dissolution current due to exposure of bare surface can be up to six orders of magnitude . ( 5 ) When the metal is in the active region any film present is only partially ...
... region of passive oxide formation the relative increase in dissolution current due to exposure of bare surface can be up to six orders of magnitude . ( 5 ) When the metal is in the active region any film present is only partially ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld