Page 11
... plating solution , current density and temperature , stirring of the plating bath , type and concentration of second phase particles , - addition agents present in the plating solution , on the amount of inert particles codeposited with ...
... plating solution , current density and temperature , stirring of the plating bath , type and concentration of second phase particles , - addition agents present in the plating solution , on the amount of inert particles codeposited with ...
Page 23
... plating baths , it may be gathered that important electrolysis parameters , such as composition of the plating bath , type of inert particles , pH of the bath and applied current density have to be considered as dependent parameters ...
... plating baths , it may be gathered that important electrolysis parameters , such as composition of the plating bath , type of inert particles , pH of the bath and applied current density have to be considered as dependent parameters ...
Page 37
... plating baths contain addition agents as brighteners and stress relievers , their suitability for composite plating is questionable . In electroless baths one of the problems to be solved is autocatalytic plating on suspended second ...
... plating baths contain addition agents as brighteners and stress relievers , their suitability for composite plating is questionable . In electroless baths one of the problems to be solved is autocatalytic plating on suspended second ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld