... pitting on the carbon steel surface had in deed occurred . It is also possible that on highly stressed surfaces , pits may nucleate cracks . The effect of pitting on surface potentials of stainless steel in a solution of HCl and FeCl3 ...
... pitting on the carbon steel surface had in deed occurred . It is also possible that on highly stressed surfaces , pits may nucleate cracks . The effect of pitting on surface potentials of stainless steel in a solution of HCl and FeCl3 ...
Page 167
... pitting of stainless steels in chloride environments Pitting is regarded as a limiting case of localized attack in which only small areas of the metal surface are attacked whilst the remainder is largely unaffected . In the laboratory ...
... pitting of stainless steels in chloride environments Pitting is regarded as a limiting case of localized attack in which only small areas of the metal surface are attacked whilst the remainder is largely unaffected . In the laboratory ...
Page 301
... pitting corrosion is expected , as in chlorine- and hypochlorite - containing alkaline solutions , the use of the Ni - Cr - Mo - type group of alloys is preferred . 3. PITTING CORROSION Pitting corrosion ( a localized - type of ...
... pitting corrosion is expected , as in chlorine- and hypochlorite - containing alkaline solutions , the use of the Ni - Cr - Mo - type group of alloys is preferred . 3. PITTING CORROSION Pitting corrosion ( a localized - type of ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld