Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 28
Page 187
... passivation , while values on the upper shelf of the curve could result in either passivation or pitting , or , in the case of strained electrodes , transgranular stress corrosion cracking . Figure 9 shows potential / oxygen curves for ...
... passivation , while values on the upper shelf of the curve could result in either passivation or pitting , or , in the case of strained electrodes , transgranular stress corrosion cracking . Figure 9 shows potential / oxygen curves for ...
Page 151
... passivation of metals in several ways , including a reduction in the kinetics of the cathodic processes occurring on the metal surface . If the anodic polarization curve of the metal exhibits an unusually active value of passivation ...
... passivation of metals in several ways , including a reduction in the kinetics of the cathodic processes occurring on the metal surface . If the anodic polarization curve of the metal exhibits an unusually active value of passivation ...
Page 338
... passivate iron effectively in the presence of oxygen . This situation can possibly be explained in terms of the insufficient cathodic depolarising power of molybdate / 25 / . When conditions are preferable for passivation the film ...
... passivate iron effectively in the presence of oxygen . This situation can possibly be explained in terms of the insufficient cathodic depolarising power of molybdate / 25 / . When conditions are preferable for passivation the film ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld