Page 239
These inhibitors have only limited applications . 1.1 . Thermodynamics of Inhibition The Pour baix diagram for iron shows that the corrosion of iron extends over a narrower range of pH at more positive potentials than at more negative ...
These inhibitors have only limited applications . 1.1 . Thermodynamics of Inhibition The Pour baix diagram for iron shows that the corrosion of iron extends over a narrower range of pH at more positive potentials than at more negative ...
Page 254
50 / showed that ' Calgon ' , a commercial inhibitor consisting of a mixture of meta and pyrophosphate , ( 75 % NaPO3 , 24 % Na4P207 ) inhibits only in the presence of oxygen and that inhibition is greatly improved by the addition of ...
50 / showed that ' Calgon ' , a commercial inhibitor consisting of a mixture of meta and pyrophosphate , ( 75 % NaPO3 , 24 % Na4P207 ) inhibits only in the presence of oxygen and that inhibition is greatly improved by the addition of ...
Page 274
Comparison of the nitrite - aminophosphonate mixture with commonly used corrosion inhibitors / 88 / . Inhibitor Corrosion rate of mild steel ( mdd ) 75 ppm aminophosphonate 15 ppm NO2 50 ppm zinc - chromate 1.7 10.8 500 ppm nitrite 17.5 ...
Comparison of the nitrite - aminophosphonate mixture with commonly used corrosion inhibitors / 88 / . Inhibitor Corrosion rate of mild steel ( mdd ) 75 ppm aminophosphonate 15 ppm NO2 50 ppm zinc - chromate 1.7 10.8 500 ppm nitrite 17.5 ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld