... inhibitor polarises the iron anodically , shifting it to the passive region . At the same time the inhibitor is reduced and the solid reduction products deposit on the weak points of the film improving its protective effect . To predict ...
... inhibitor polarises the iron anodically , shifting it to the passive region . At the same time the inhibitor is reduced and the solid reduction products deposit on the weak points of the film improving its protective effect . To predict ...
Page 254
... inhibitor consisting of a mixture of meta and pyrophosphate , ( 75 % NaPO3 , 24 % Na4P207 ) inhibits only in the presence of oxygen and that inhibition is greatly improved by the addition of calcium ions ( Figure 4 ) . Later Lahodny ...
... inhibitor consisting of a mixture of meta and pyrophosphate , ( 75 % NaPO3 , 24 % Na4P207 ) inhibits only in the presence of oxygen and that inhibition is greatly improved by the addition of calcium ions ( Figure 4 ) . Later Lahodny ...
Page 274
... inhibitors / 88 / . Inhibitor Corrosion rate of mild steel ( mdd ) 75 ppm aminophosphonate 15 ppm NO2 50 ppm zinc - chromate 1.7 10.8 500 ppm nitrite 17.5 100 ppm zinc - phosphonate 5.8 However , the formulation can be used successfully ...
... inhibitors / 88 / . Inhibitor Corrosion rate of mild steel ( mdd ) 75 ppm aminophosphonate 15 ppm NO2 50 ppm zinc - chromate 1.7 10.8 500 ppm nitrite 17.5 100 ppm zinc - phosphonate 5.8 However , the formulation can be used successfully ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld