Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 82
Page 119
... influence of Art implants 126 ( ü ) The influence of metal ion implants 128 ( iü ) The influence of metal ion implants on electrochemical polarization behaviour 133 ( iv ) The influence of metal ion implants on current decay transients ...
... influence of Art implants 126 ( ü ) The influence of metal ion implants 128 ( iü ) The influence of metal ion implants on electrochemical polarization behaviour 133 ( iv ) The influence of metal ion implants on current decay transients ...
Page 133
... influence on the propensity to cracking of ferritic steels in the carbonate - bicarbonate solution . ( iü ) The influence of metal ion implants on electrochemical polarization behavior . The anodic polarization curves for implanted and ...
... influence on the propensity to cracking of ferritic steels in the carbonate - bicarbonate solution . ( iü ) The influence of metal ion implants on electrochemical polarization behavior . The anodic polarization curves for implanted and ...
Page 178
... influence of the bulk alloyed element is in some way related to its influence on reducing the number of potential pitting sites rather than on its influence in increasing the passive nature of the alloy . 10. In 20 wt % H2SO4 Mo ...
... influence of the bulk alloyed element is in some way related to its influence on reducing the number of potential pitting sites rather than on its influence in increasing the passive nature of the alloy . 10. In 20 wt % H2SO4 Mo ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld