Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 8
Page 84
... grain boundary analyses of the steel after heat treatment to 823 K for different times are shown in Table 2. The ... grain boundaries , and the standard deviations are also shown . Specimen A , heated at 823 K for 10 min . , did not ...
... grain boundary analyses of the steel after heat treatment to 823 K for different times are shown in Table 2. The ... grain boundaries , and the standard deviations are also shown . Specimen A , heated at 823 K for 10 min . , did not ...
Page 91
... grain boundary phosphorus coverage , shown in Fig . 4. This dependence is only valid since the grain boundary concentrations of all cther segregated elements are approximately invariant with time of heat treatment at 823 K. The crack ...
... grain boundary phosphorus coverage , shown in Fig . 4. This dependence is only valid since the grain boundary concentrations of all cther segregated elements are approximately invariant with time of heat treatment at 823 K. The crack ...
Page 133
... grain boundary heterogeniety of the steels and therefore , the distribution of local galvanic cells . The consequence being that when the alloying species are introduced by implantation , they do not influence the boundary of Corrosion ...
... grain boundary heterogeniety of the steels and therefore , the distribution of local galvanic cells . The consequence being that when the alloying species are introduced by implantation , they do not influence the boundary of Corrosion ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld