Page 241
... Formed on Iron and Low Carbon Steels The composition and the structure of the films formed on iron and mild steels in inhibited neutral to basic solutions have been widely investigated in the last fifteen years . The emerging view is ...
... Formed on Iron and Low Carbon Steels The composition and the structure of the films formed on iron and mild steels in inhibited neutral to basic solutions have been widely investigated in the last fifteen years . The emerging view is ...
Page 242
... formed on iron in a solution of 0.1 M Na3AsO4 , pH 8.5 at open circuit potential consisted of iron oxide with ferric arsenate and some deposited elemental arsenic , indicating that cathodic reduction of arsenate does occur . Lumsden / 9 ...
... formed on iron in a solution of 0.1 M Na3AsO4 , pH 8.5 at open circuit potential consisted of iron oxide with ferric arsenate and some deposited elemental arsenic , indicating that cathodic reduction of arsenate does occur . Lumsden / 9 ...
Page 252
... formed film prior to immersion in solutions of pH 7-12 , the resulting film has some protective ability which is mainly due to the presence of iron oxide . Results concerned with the composition of the films formed on iron in aerated ...
... formed film prior to immersion in solutions of pH 7-12 , the resulting film has some protective ability which is mainly due to the presence of iron oxide . Results concerned with the composition of the films formed on iron in aerated ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld