Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 80
Page 141
... fatigue crack initiation It has been suggested by a number of workers that corrosion pits can be precursors to the initiation of stress corrosion / 189-191 / and corrosion fatigue cracks / 181,192-196 / . In a review of fatigue crack ...
... fatigue crack initiation It has been suggested by a number of workers that corrosion pits can be precursors to the initiation of stress corrosion / 189-191 / and corrosion fatigue cracks / 181,192-196 / . In a review of fatigue crack ...
Page 145
... crack walls , ( 3 ) corrosion blunting of the crack tip , ( 4 ) variation in the rate of uptake of hydrogen into the ... fatigue crack . In previous chapters the state of knowledge of the solution composition and electrode potential in ...
... crack walls , ( 3 ) corrosion blunting of the crack tip , ( 4 ) variation in the rate of uptake of hydrogen into the ... fatigue crack . In previous chapters the state of knowledge of the solution composition and electrode potential in ...
Page 195
The fatigue crack propagation for both steels showed that the environmental enhancement of fatigue crack growth rates increases as the frequency of testing was decreased , using either sine or triangular wave forms . A general trend in ...
The fatigue crack propagation for both steels showed that the environmental enhancement of fatigue crack growth rates increases as the frequency of testing was decreased , using either sine or triangular wave forms . A general trend in ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld