From inside the book
Results 1-3 of 78
Page 280
The resistance to uniform corrosion in oxidizing or nonoxidizing environments is directly related to chromium or molybdenum content, respectively. Pitting corrosion resistance is determined by the compositional variable (Cr % + 2.4 Mo ...
The resistance to uniform corrosion in oxidizing or nonoxidizing environments is directly related to chromium or molybdenum content, respectively. Pitting corrosion resistance is determined by the compositional variable (Cr % + 2.4 Mo ...
Page 293
Oxidizing Environments > Oxidizing environments are generally characterized by a redox reaction where a soluble species other than it is reduced . Some common species include NO2 , Cr20 ; 2 , Mn0a , Fet3 , Cu + 2 , and oxygen .
Oxidizing Environments > Oxidizing environments are generally characterized by a redox reaction where a soluble species other than it is reduced . Some common species include NO2 , Cr20 ; 2 , Mn0a , Fet3 , Cu + 2 , and oxygen .
Page 310
Sour Gas Environments In the absence of oxygen , all of the nickel - base alloys exhibit excellent stress corrosion cracking resistance with no failures reported in CO2 / H2S / C1 environments , up to 500 ° F . These alloys become ...
Sour Gas Environments In the absence of oxygen , all of the nickel - base alloys exhibit excellent stress corrosion cracking resistance with no failures reported in CO2 / H2S / C1 environments , up to 500 ° F . These alloys become ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld