From inside the book
Results 1-3 of 82
Page 221
The double - U - bend samples with the graphite wool sandwich , although exposed to the severest testing environment - airsaturated water at 525 ° F to 550 ° F - showed no indication of TGSCC , even after long exposure periods .
The double - U - bend samples with the graphite wool sandwich , although exposed to the severest testing environment - airsaturated water at 525 ° F to 550 ° F - showed no indication of TGSCC , even after long exposure periods .
Page 195
The fatigue crack propagation for both steels showed that the environmental enhancement of fatigue crack growth rates ... Distilled water and the 3 % NaCl environment at open circuit potential led to enhancement of fatigue crack growth ...
The fatigue crack propagation for both steels showed that the environmental enhancement of fatigue crack growth rates ... Distilled water and the 3 % NaCl environment at open circuit potential led to enhancement of fatigue crack growth ...
Page 280
The resistance to uniform corrosion in oxidizing or nonoxidizing environments is directly related to chromium or molybdenum content, respectively. Pitting corrosion resistance is determined by the compositional variable (Cr % + 2.4 Mo ...
The resistance to uniform corrosion in oxidizing or nonoxidizing environments is directly related to chromium or molybdenum content, respectively. Pitting corrosion resistance is determined by the compositional variable (Cr % + 2.4 Mo ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld