Corrosion Reviews, Volumes 5-6Scientific Publications Division, Freund Publishing House, 1982 |
From inside the book
Results 1-3 of 86
Page 174
... dissolved oxygen curves were developed . The studies showed that carbon steels were susceptible to Transgranular Stress Corrosion Cracking ( TGSCC ) in pure water . At elevated temperatures , increasing the concentration of dissolved ...
... dissolved oxygen curves were developed . The studies showed that carbon steels were susceptible to Transgranular Stress Corrosion Cracking ( TGSCC ) in pure water . At elevated temperatures , increasing the concentration of dissolved ...
Page 184
... dissolved oxygen was studied in detail for all three steels , all of the data will not be given . Instead , summaries and comparisons will be presented . Often there was little difference between measured potentials for the different ...
... dissolved oxygen was studied in detail for all three steels , all of the data will not be given . Instead , summaries and comparisons will be presented . Often there was little difference between measured potentials for the different ...
Page 218
... dissolved oxygen . After 1500 hours of additional exposure , the U - bends were removed and reexamined . A thick oxide had formed on all the specimens ; although the surfaces appeared pitted , stress corrosion cracking had not occurred ...
... dissolved oxygen . After 1500 hours of additional exposure , the U - bends were removed and reexamined . A thick oxide had formed on all the specimens ; although the surfaces appeared pitted , stress corrosion cracking had not occurred ...
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld