Page 153
It has been shown experimentally and theoretically that the buffering reactions in sea water have very little effect on the pH conditions in static cracks or crevices except where calcareous deposition was likely .
It has been shown experimentally and theoretically that the buffering reactions in sea water have very little effect on the pH conditions in static cracks or crevices except where calcareous deposition was likely .
Page 154
Calcareous deposition Calcareous deposition on the walls of the crack can occur when the pH in the crack exceeds 8.2 and this will be expected on polarising steel in sea water to negative potentials . Calcareous deposition can result in ...
Calcareous deposition Calcareous deposition on the walls of the crack can occur when the pH in the crack exceeds 8.2 and this will be expected on polarising steel in sea water to negative potentials . Calcareous deposition can result in ...
Page 44
A suitable material is Si , both in crystalline and amorphous state , deposited by chemical vapour deposition ( CVD ) / 17 , 77-79 ) . These coatings are extremely stable ( up to 800 ° C ) and have absorptances of about 0.8 and ...
A suitable material is Si , both in crystalline and amorphous state , deposited by chemical vapour deposition ( CVD ) / 17 , 77-79 ) . These coatings are extremely stable ( up to 800 ° C ) and have absorptances of about 0.8 and ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
CONTENTS | 2 |
PRODUCTION OF ELECTROLESS COMPOSITE COATINGS | 23 |
INDUSTRIAL APPLICABILITY OF COMPOSITE COATINGS | 30 |
Copyright | |
6 other sections not shown
Other editions - View all
Common terms and phrases
acid active addition alloys aluminium analysis anodic application associated bulk carbon chemical chloride coatings composition concentration considered containing corrosion fatigue corrosion rates crack tip crevice critical current density curves decrease dependent deposition developed dissolution effect electrochemical electrode elements Energy Engineering environments experimental experiments factor failure fatigue crack Figure film formed grain boundary heat hydrogen implanted important increase indicated influence inhibition inhibitor initial ions iron journal layer materials measurements mechanism metal molybdate molybdenum observed obtained occur oxide oxygen particles passive plating position possible potential present production properties protection published range reaction reduction region reported resistance respect REVIEWS selective shown shows significant Solar solution species specimen stainless steel strain stress corrosion cracking structural studies surface Table technique temperature tests tion values weld